| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | Mo | N |
| GB/T 3280-2015 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| JIS G 4305 | 0.03 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | |
| ASTM A240 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | ||||
| Mpa | Mpa | 50mm | HBW | HRB | HV | ||||
| GB/T 3280-2015 | 485 | 180 | 40 | 217 | 95 | 220 | ------ | ||
| JIS G 4305 | 480 | 175 | 40 | 187 | 90 | 200 | ------ | ||
| ASTM A240 | 485 | 170 | 40 | 217 | 95 | ------ | |||
| 316L | |||||||||
| Thickness | 0.05-3mm | ||||||||
| Width | 4.6-1500mm | ||||||||
| Length | As required | ||||||||
| Surface | 2B，NO.4，BA，4K，HL，8K,SB | ||||||||
| Original | DSM | ||||||||
| Standard | Produce as per your requirement. | ||||||||
| MOQ | 2tons.We also can accept sample order. | ||||||||
| Application | Exhaust manifolds /Furnace parts /Heat exchangers | ||||||||
| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | Mo | N |
| GB/T 3280-2015 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| JIS G 4305 | 0.03 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | |
| ASTM A240 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | ||||
| Mpa | Mpa | 50mm | HBW | HRB | HV | ||||
| GB/T 3280-2015 | 485 | 180 | 40 | 217 | 95 | 220 | ------ | ||
| JIS G 4305 | 480 | 175 | 40 | 187 | 90 | 200 | ------ | ||
| ASTM A240 | 485 | 170 | 40 | 217 | 95 | ------ | |||
| 316L | |||||||||
| Thickness | 0.05-3mm | ||||||||
| Width | 4.6-1500mm | ||||||||
| Length | As required | ||||||||
| Surface | 2B，NO.4，BA，4K，HL，8K,SB | ||||||||
| Original | DSM | ||||||||
| Standard | Produce as per your requirement. | ||||||||
| MOQ | 2tons.We also can accept sample order. | ||||||||
| Application | Exhaust manifolds /Furnace parts /Heat exchangers | ||||||||